Does anyone know if grain oriented electrical steel could deliver superior magnetic field strength over traditional solid cores? Because of the lamination of electrical steel you are obviously using slightly less ferrous material due to the insulation layers, but it is grain oriented. Grain oriented electrical steel to my knowledge can deliver 30% more flux compared to non oriented electrical steel. Just wondering if anyone had any knowledge on this.