I do not think they will mind if we repeat it here. Saves people with no interest in their forum joining to read this.
New website is
Machinable Wax
-----------------------------------------------------------
Found this website:
**broken link removed** they
have a great description on how to make machinable wax at home. All you
basically do is melt LDPE in a deep fat fryer full of paraffin wax. Basically
you raise raise 4lb of paraffin wax to 95C for LDPE or 110C for HDPE. You then
add 1 lb of LDPE or HDPE very slowly. Any amount can be made. Considering the
limitations of a Maker bot drimel toolhead, this could be a great substrait.
The store this is from looks like it's dying, so I will quote it here:
"You may be looking for a cost effective solution for machinable wax.
One basic composition of machinable wax is simply standard parrafin wax,
available at most craft stores, and polyethylene.
What is polyethylene? Its most basic description is that it is a thermoplastic
and it is derived from petroleum. The two main types are Low Density and High
Density polyethylene, commonly referred to as LDPE and HDPE respectively. The
following is a list of common LDPE/HDPE items:
* Grocery store bags
* Garbage Bags
* Paint drops (plastic sheets)
* Lawn Chairs
* Cutting Boards
* Plastic Lumber
* Milk Jugs
* Commercial Bathroom stalls
One of THE most common uses is in plastic grocery store bags. This is also
probably the best source of LDPE/HPDE for use in making homemade machinable
wax. Its readily available as most people have 50 or so stuffed away in a
pantry or cabinet. Perfect to make a little machinable wax with.
Alternate sources for use in a machinable wax recipe, would be plastic drop
clothes used in painting. They can be purchased at most home improvement
stores.
Most plastics are usually marked with LDPE or HDPE and have a number 4 or 2
(respectively) located on recyclable polyethylene.
In general its easier to melt down LDPE for use in machinable wax. LDPE has a
lower melting point, and hence mixes better with the parrafin. LDPEs melting
point for continuous heat is 203F (95C). HDPEs melting point with continuous
heat is 230F(110C). It may be helpful to note that in general Target uses LDPE
and Walmart uses HDPE.
What to use for melting??? You everyday kitchen cooker will work fine. Its
HIGHLY recommended that you dedicate a cooker to your machinable wax recipe.
Temperature control that lists numbers is better than just lo/med/high. Do not
use a double boiler, they generally only get up to 212F(97C). Thats only barely
hot enough to melt LDPE, and it would take a lot longer.
So you have your block of candle wax, a few handfulls of grocery store bags,
and a cooker. A METAL kitchen strainer will be very helpful as well. The large
ones used for pasta noodles are best. You also need a mold to poor your
machinable wax into. Use metal molds, plastic tupperware will melt or warp from
the heat.
The general machinable wax recipe is a 4:1 ratio of parrafin wax to LDPE/HDPE.
Your machinable wax recipe could vary depending on how hard or soft you want
the wax to be. Obviously, the more plastic you add the harder it will get. But
like sugar in a glass of tea, eventually the polyethylene will stop disolving
and you will get large clumps of polyethylene form in the pot. If you poor it
in a pan without straining it, it will look like goo in your wax and will not
carve very well.
We will use a 4lb wax to 1lb LDPE in this machinable wax recipe example. So you
will end up with about 5 lbs of machinable wax.
Start out by melting the wax in the pot. Get it good and hot, about 250-275F,
max 275F.
Once youve reached temp, start feeding in small pieces of the plastic. If you
can, cut up the plastic into small strips before feeding it in. It will melt
better and more consistently than just dumping whole bags in. Stir constantly
and use good ventilation.
You will know youve added enough because the plastic will stop melting as well.
It will start balling up into clumps.
Now you can use the kitchen strainer, poor your wax through the strainer into
your mold. This will remove any unwanted clumps from the mix.
For cooling, try to slow down the cooling as much as possible. You can wrap the
mold with an old blanket, or use a small space heater to keep the area around
the mold warm. Some warping is unavoidable. You can either plane the finished
product, or use a CNC router to shave down the top.
You will be left with a good quality machinable wax. Refine your machinable wax
recipe. You may try different types of wax, or different types of polyethylene
in your recipe.
We also offer kits of shaved LDPE and HDPE. Our kits are sold by weight and use
LDPE/HDPE shavings that will melt better than most types of plastic you may
find."